Spark Testable High Temperature Trowelable Abrasion Control Compound
An advanced ceramic composite formulated to protect equipment from corrosion and erosion in elevated temperature water solution immersion. ARC HT-T is applied at a nominal thickness of 900 - 1150 microns (35 -45 mils). The cured product provides outstanding blister and abrasion resistance with a high gloss finish.
|
|
| Dry Temperature Dry (Min/Max) |
-20 F (-29C) to 320 F (150 C)
|
|
| Wet Temperature (Min/Max) |
-20 F (-29C) to 230 F (110 C)
|
|
| Compressive Strength - kg/cm2 - Mpa (psi) |
949 - 93 (13,500)
|
|
| Flexural Strength - kg/cm2 - Mpa (psi) |
548 -54 (7,800)
|
|
| Tensile Strength - kg/cm2/Mpa (psi) |
323 - 32 (4,600)
|
|
| Tensile Adhesion - kg/cm2 - Mpa (psi) |
Greater than 140 - 14 (2,000)
|
|
| Impact Resistance - nt m (in. lbs.) |
45, (40)
|
|
|
|
|