100% Novolac acid resistant coating
An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. A two-coat application of ARC 982 provides protection from concentrated acids, alkalies, and solvents. A low viscosity composite that is applied by brush, squeegee, or a plural component sprayer system. ARC 982 may be applied at a minimum thickness of 250 microns (10 mils) per coat.
|
Dry Temperature Dry (Min/Max) |
-20 F (-29C) to 350 F (175 C)
|
|
Wet Temperature (Min/Max) |
-20 F (-29C) to 160 F (70 C) |
|
Compressive Strength - kg/cm2 - Mpa (psi) |
872 - 85 (12,400) |
|
Flexural Strength - kg/cm2 - Mpa (psi) |
312 -31 (4,440)
|
|
Tensile Strength - kg/cm2/Mpa (psi) |
250 - 24 (3,500)
|
|
Tensile Adhesion - kg/cm2 - Mpa (psi) |
Greater than 193 -19 (2,750) |
|
|
|
|