Fine Grade Sliding Wear Compound
ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. ARC 897 can be used either to rebuild eroded metal surfaces or to provide a wear resistant, sacrificial surface which frequently outperforms the original metal, rubber liners, ceramic tiles or weld overlay. ARC 897 is a long lasting wearing surface and is chosen over ARC 890 where a thinner, more easily applied composite is required. It is applied at a thickness of 3 mm (1/8 inch) or more.
|
|
| Dry Temperature Dry (Min/Max) |
-20 F (-29C) to 400 F (205 C)
|
|
| Wet Temperature (Min/Max) |
-20 F (-29C) to 205 F (95 C) |
|
| Compressive Strength - kg/cm2 - Mpa (psi) |
950 - 93 (13,500) |
|
| Flexural Strength - kg/cm2 - Mpa (psi) |
690 -68 (9,800)
|
|
| Tensile Strength - kg/cm2/Mpa (psi) |
340 - 33 (4,800)
|
|
| Tensile Adhesion - kg/cm2 - Mpa (psi) |
Greater than 123 - 12 (1,750) |
|
| Impact Resistance - nt m (in. lbs.) |
6,0 (53) |
|
|
|
|