Coarse Grade Sliding Wear Compound
An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It can be used either to rebuild eroded metal surfaces or to provide a wear resistant surface, which frequently outperforms the original metal, weld overlay, rubber liners or ceramic tiles. It is normally applied at a thickness of 6 mm (1/4 inch) or more.
|
|
| Dry Temperature Dry (Min/Max) |
-20 F (-29C) to 400 F (205 C)
|
|
| Wet Temperature (Min/Max) |
-20 F (-29C) to 205 F (95 C) |
|
| Compressive Strength - kg/cm2 - Mpa (psi) |
620 - (8,800) |
|
| Flexural Strength - kg/cm2 - Mpa (psi) |
370 - (5,200)
|
|
| Tensile Strength - kg/cm2/Mpa (psi) |
250 - 25 (3,500)
|
|
| Tensile Adhesion - kg/cm2 - Mpa (psi) |
Greater than 123 - 12 (1,750) |
|
| Impact Resistance - nt m (in. lbs.) |
6,8 (60) |
|
|
|
|