Paste grade machinable composite
A reinforced composite for the repair and protection of metal surfaces. The ARC 10 is formulated for applications where machining to exact tolerances is required or desired. It is frequently used as an alternative to resurfacing by welding or flame spraying. It is non-sagging, non-shrinking, and 100% solids
|
|
| Dry Temperature Dry (Min/Max) |
-20 F (-29C) to 200 F (93 C)
|
|
| Wet Temperature (Min/Max) |
-20 F (-29C) to 150 F (66 C) |
|
| Compressive Strength - kg/cm2 - Mpa (psi) |
930 - 93 (13,000) |
|
| Flexural Strength - kg/cm2 - Mpa (psi) |
710 - 71 (10,000)
|
|
| Tensile Strength - kg/cm2/Mpa (psi) |
280 - 28 (4,000)
|
|
| Tensile Adhesion - kg/cm2 - Mpa (psi) |
Greater than 123 - 12 (1,750) |
|
|
|
|